Ferric oxide desulfurizer

Efficient Ferric oxide desulfurizer GB ISO9001:2008 Gas, oil desulfurizer removing H2S AAA credit Level

As our latest chemical reagent for desulfurization(removing sulfur), TC-10X Ferric Oxide Desulfurizer was invented by our company under Professor Pang's  (from Zhengzhou University) instruction. It is synthesized into extrudates from molysite  ferric oxide, manganate and manganese oxide, by adding certain compound assistant catalysts & binder.

LYT-311C Desulfurizer is mainly used in the removing of H2S from the feedstock of petroleum refining, coal chemical organic synthesis, chemical fertilizer and chemical fiber industries.

Also, it's convenient to for application, energy saving and easy to be reactivated.

1.The Technical Parameters of TC-10X Ferric Oxide    Desulfurizer.

   

Model	TC-101	TC-102	TC-103
appearance	claybank columnars	claybank columnars	claybank columnars
Size(mm)	4.5-5.5	4.5-5.5	4.5-5.5
Length(mm)	5-15	5-15	5-15
intensity	≥45	≥42	≥35
Bulk density(kg/L)	0.72-0.80	0.75-0.80	0.75-0.85
sulfur capacity	≥40%	≥35%	≥30%
Desulfurization  precision	≤0.1	≤0.5	≤1.0

 2.The theories of the desulfurization and regeneration of TC-10X ferric oxide desulfurizer.

chemical reaction formula:

Desulfurization: Fe2O3.H2O+3H2S=Fe2S3.H2O+3H2O  Regenerating:  2Fe2S3.H2O+3O2=2Fe2O3.H2O+6S   The regeneration is a strong exothermic reactionIf there is O2  in the air,or O2/H2S≥2.5,the desulfuration and regeneration will be a continuous reacting process,those two formular can be merged into one: 2H2S+O2=H2O+2S.the ferric oxide act as the catalyst in fact.

3.The main features of TC -10X ferric oxide desulfurizer

    1.High speed of desulfurizing.

The space velocity is 1000~3000h-1, , and the breakthrough velocity   is  6000h-1,2-4 time faster than common ferric oxide’air speed(300h-1).

 2.High breakthrough capacity

In conditions:

Speed velocity:1000h-1         atmospheric condition

Initial H2S:1%  Final H2S:≤5×10-8

The breakthrough capacity is 25%

4. TC -10X ferric oxide desulfurizer has high resistance to   abrasion and  water.

It will not pulverize or soften, neither when  boiled  for two hours or put in water for 30 days, or under alternated pressure of 12MPa and sudden relief of pressure.   

5.Advised Application condition of TC -10X ferric oxide desulfurizer.11. H2S≤15mg/Nm3      

   space velocity:  1000~3000h-1

 2.H2S≥15mg/Nm3 

     space velocity:300~1000h-13.Temperature: 0~100°C

4.Pressure:common pressure-10MPa

5.Humidity level: 20~100%,but it is seriously prohibited from wet beds.

Ferric oxide desulfurizer